Contain	Code	Percent%
Cesium tungsten oxide	52350-17-1	~ 6
1-Methoxy-2-Propanol	107-98-2	~ 18
Nhựa Acrylic	123-86-4	10 ~ 23
Butyl Acetate	2440-22-4	10 ~ 23
2-(2H-Benzotriazol-2-yl)-p-cresol		~ 7
Ethylene Glycol Monobutyl Ether Acetate	112-07-2	~ 38

Technical Data Sheet

1. Heat insulation

IRUV CUT COAT test report-001 NSG Techno-Research Corporation June 2003.

“Optical properties and thermal characterization of coated glass”

Visible light transmission	Transmittance sunshine	Solar reflectance	Solar radiation Absorption rate	UV transmittance
68.0%	39.9%	5.0%	55.1%	0.33%

Solar heat gain rate		Shading coefficient
Summer	Winter	Summer	Winter
0.59	0.56	0.67	0.63

2. Heat resistant cracking

IRUV CUT COAT test report-001 NSG Techno-Research Corporation June 2003.

“Thermal cracking test”

Direction	East		Southeast		South
Thermal cracking judgment	OK		OK		OK
Season	Summer	Winter	Summer	Winter	Summer	Winter
Temperature of central portion (0C)	44	4	46	24	36	26
Sash temperature (0C)	25	-10	27	7	27	7
Thermal stress occurs (kg/cm2)	125	89	125	125	54	125
Allowable thermal stress (kg/cm2)	180	180	180	180	180	180
Heat stress difference (kg/cm2)	44	91	55	55	126	55

Direction	Southwest		West
Thermal cracking judgment	OK		OK
Season	Summer	Winter	Summer	Winter
Temperature of central portion (0C)	47	26	47	18
Sash temperature (0C)	28	7	28	4
Thermal stress occurs (kg/cm2)	125	125	125	90
Allowable thermal stress (kg/cm2)	180	180	180	180
Heat stress difference (kg/cm2)	55	55	55	90

3. Adhension

KOKANKYO Engineering Co., Ltd. In April 2006

“Weather resistant coating agent test report”

Item	Method	Result	Standard
Boiling water resistance	1 hour boiling water immersion	Ο
Gasoline resistance	Gasoline rubbing 200	Ο
Solvent resistance	Xylem rubbing 200	Ο
	0.1 sodium hydroxide	Ο
Chemical resistance	5% sodium hydroxide	X
	10% nitric acid	Ο
	10% sulfuric acid	Ο
Scratch hardness	Pencil method	9H	JIS K5400
Adhension	Cross-cut adhension test	100/100	JIS K5400

4. Durability

KOKANKYO Engineering Co., Ltd. in April 2006

“Weather resistant coating agent test report”

Tested by a xenon lamp weather over (equivalent to approximately 10 years) 2580 hours

Test Result

The change is not accepted by a color, a film

March, 2008 DAINICHISEIKA Color & Chemicals Mfg, Co., Ltd.

Super UV irradiation testing and pencil hardness test

Yellowing, cloudiness and evaluation

	Blank	100 hour	200 hour
Sample 1	Ο	Ο	Ο
Sample 2	Ο	Ο	Ο

Pencil hardness test (JIS K5400)

	Blank	100 hour	200 hour
Sample 1	4H	4H	4H
Sample 2	4H	4H	4H

5. Safety

• Volatile Organic Compounds (VOC)

Japan Food Research Laboratories Co., Ltd. In August 2006

“Formaldehyde test”

Analysis of test items	Test result	Detection limit		Method
Formaldehyde emission	0.12mg/L		­Note (*)	Absorption spectrophotometer

­(*) Note 1. JIS K5601-4-1: 2003

6. Combustion test

Japan Railway Rolling Stock & Machinery Association in October 2004

Test number 16-526K

During combustion of alcohol		After combustion of alcohol
Ignition	No	After flame	-
Wear flame	No	Residual dust	-
Smoke	No	Carbonization	60mm discoloration
Force of flame	-	Deformation	No
Remarks
Remarks
Assessment		Non-combustible

Tested with No.151 Ordinance of the “Ministry of Land, Infrastructure, Transport and Tourism”

7. Save Electricity Cost

KOKANKYO Engineering Co., Ltd. in October 2005

Sheet electricity costs for the first year of use conditioner (15 yen / kWh)

Exchange Rate 11/2013: 1 Yen = 200 VNĐ

Name	Normal Glass	Glass with the Insulating IRUV Cut Coat H-SC
Conditioner	639,278 Yen (127,855,600 VND)	544,521 Yen (108,904,200 VNĐ)
Deviation’s electricity cost		- 94,756 Yen - (18,951,200 VNĐ)
		Down 16%